Scientists show point defects in cathode crystals may speed lithium absorption

Detours may make batteries better
An illustration shows a battery's cathode undergoing phase transition from iron phosphate (FP) to lithium iron phosphate (LFP) during charging. Simulations by Rice University scientists showed that adding defects -- distortions in their crystal lattices -- could help batteries charge faster. Credit: Kaiqi Yang/Rice University

Here's a case where detours speed up traffic. The result may be better batteries for transportation, electronics and solar energy storage.

Scientists at Rice University's Brown School of Engineering have discovered that placing specific defects in the crystalline lattice of iron phosphate-based cathodes broadens the avenues through which lithium ions travel. Their theoretical calculations could improve performance up to two orders of magnitude and point the way to similar improvements in other types of batteries.

These defects, known as antisites, are formed when atoms are placed at the wrong positions on the lattice—that is, when iron atoms sit on the sites that should be occupied by lithium. Antisite defects impede lithium movement inside the crystal lattice and are usually considered detrimental to battery performance.

In the case of lithium iron phosphate, however, the Rice researchers discovered they create many detours within the and enable lithium ions to reach the reaction front over a wider surface, which helps improve the charge or discharge rate of the batteries.

The research appears in the Nature journal Computational Materials.

Detours may make batteries better
Rice University graduate student Kaiqi Yang, left, and materials scientist Ming Tang modeled how engineering defects in the atomic lattice of an iron phosphate cathode can improve the performance of lithium ion batteries. Credit: Jeff Fitlow/Rice University

Lithium iron phosphate is a widely used for and also serves as a good model system for studying the physics underlying the battery cycling process, said Rice materials scientist Ming Tang, who carried out the research with alumnus Liang Hong, now a researcher at MathWorks, and graduate student Kaiqi Yang.

Upon lithium insertion, the cathode changes from a lithium-poor phase to a lithium-rich one, said Tang, an assistant professor of materials science and nanoengineering. When the surface reaction kinetics are sluggish, lithium can only be inserted into within a narrow surface region around the phase boundary—the "road"—a phenomenon that limits the speed at which the battery can recharge.

"If there are no defects, lithium can only enter this small region right around the phase boundary," he said. "However, antisite defects can make lithium insertion take place more uniformly across the surface, and so the boundary would move faster and the battery would charge faster.

"If you force the defect-free cathode to be charged fast by applying a large voltage, there will be a very high local lithium flux at the surface and this can cause damage to the cathode," he said. "This problem can be solved by using defects to spread the flux over the entire cathode surface."

Annealing the material—heating without burning it—could be used to control the concentration of defects. Tang said defects would also allow larger cathode particles than nanoscale crystals to be used to help improve energy density and reduce surface degradation.

A cathode undergoes phase transition from iron phosphate (FP) to lithium iron phosphate (LFP) when charged. Rice scientists showed that adding defects to their crystal lattices could help batteries charge faster, as the top animation shows. Credit: Kaiqi Yang

"An interesting prediction of the model is that this optimal configuration depends on the shape of the particles," he said, "We saw that facets of a certain orientation could make the detours more effective in transporting lithium ions. Therefore, you will want to have more of these facets exposed on the cathode ."

Tang said the model could be applied as a general strategy to improve phase-changing battery compounds.

"For structural materials like steel and ceramics, people play with defects all the time to make materials stronger," he said. "But we haven't talked much about using defects to make better battery materials. Usually, people see defects as annoyances to be eliminated.

"But we think we can turn defects into friends, not enemies, for better energy storage."


Explore further

Study reveals unknown details about common lithium-ion battery materials

More information: Liang Hong et al, A mechanism of defect-enhanced phase transformation kinetics in lithium iron phosphate olivine, npj Computational Materials (2019). DOI: 10.1038/s41524-019-0255-3
Provided by Rice University
Citation: Scientists show point defects in cathode crystals may speed lithium absorption (2019, December 9) retrieved 21 February 2020 from https://phys.org/news/2019-12-scientists-defects-cathode-crystals-lithium.html
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.
39 shares

Feedback to editors

User comments