Stress test reveals graphene won't crack under pressure

Stress test reveals graphene won't crack under pressure
Teng Cui holds up a silicon chip with half a million embedded tiny holes. By stretching graphene across the holes, Cui was able to measure its resistance to mechanical fatigue. Credit: Daria Perevezentsev/University of Toronto Engineering

Graphene is a paradox. It is the thinnest material known to science, yet also one of the strongest. Now, research from University of Toronto Engineering shows that graphene is also highly resistant to fatigue—able to withstand more than a billion cycles of high stress before it breaks.

Graphene resembles a sheet of interlocking hexagonal rings, similar to the pattern you might see in bathroom flooring tiles. At each corner is a single carbon atom bonded to its three nearest neighbours. While the sheet could extend laterally over any area, it is only one atom thick.

The intrinsic strength of has been measured at more than 100 gigapascals, among the highest values recorded for any material. But materials don't always fail because the load exceeds their maximum strength. Stresses that are small but repetitive can weaken materials by causing microscopic dislocations and fractures that slowly accumulate over time, a process known as .

"To understand fatigue, imagine bending a metal spoon," says Professor Tobin Filleter, one of the senior authors of the study, which was recently published in Nature Materials. "The first time you bend it, it just deforms. But if you keep working it back and forth, eventually it's going to break in two."

The research team—consisting of Filleter, fellow University of Toronto Engineering professors Chandra Veer Singh and Yu Sun, their students, and collaborators at Rice University—wanted to know how graphene would stand up to repeated stresses. Their approach included both physical experiments and .

"In our atomistic simulations, we found that cyclic loading can lead to irreversible bond reconfigurations in the graphene lattice, causing catastrophic failure on subsequent loading," says Singh, who along with postdoctoral fellow Sankha Mukherjee led the modelling portion of the study. "This is unusual behaviour in that while the bonds change, there are no obvious cracks or dislocations, which would usually form in metals, until the moment of failure."

Ph.D. candidate Teng Cui, who is co-supervised by Filleter and Sun, used the Toronto Nanofabrication Centre to build a physical device for the experiments. The design consisted of a silicon chip etched with half a million tiny holes only a few micrometres in diameter. The graphene sheet was stretched over these holes, like the head of a tiny drum.

Using an , Cui then lowered a diamond-tipped probe into the hole to push on the graphene sheet, applying anywhere from 20 to 85 percent of the force that he knew would break the material.

Stress test reveals graphene won't crack under pressure
University of Toronto Engineering researchers used an atomic force microscope (pictured) to measure the ability of graphene to resist mechanical fatigue. They found that the material can withstand more than a billion cycles of high stress before breaking. Credit: Daria Perevezentsev/University of Toronto Engineering

"We ran the cycles at a rate of 100,000 times per second," says Cui. "Even at 70 percent of the maximum stress, the graphene didn't break for more than three hours, which works out to over a billion cycles. At lower stress levels, some of our trials ran for more than 17 hours."

As with the simulations, the graphene didn't accumulate cracks or other tell-tale signs of stress—it either broke or it didn't.

"Unlike metals, there is no progressive damage during fatigue loading of graphene," says Sun. "Its failure is global and catastrophic, confirming simulation results."

The team also tested a related material, graphene oxide, which has small groups of atoms such as oxygen and hydrogen bonded to both the top and bottom of the sheet. Its fatigue behaviour was more like traditional materials, in that the failure was more progressive and localized. This suggests that the simple, regular structure of graphene is a major contributor to its unique properties.

"There are no other materials that have been studied under fatigue conditions that behave the way graphene does," says Filleter. "We're still working on some new theories to try and understand this."

In terms of commercial applications, Filleter says that graphene-containing composites—mixtures of conventional plastic and graphene—are already being produced and used in sports equipment such as tennis rackets and skis.

In the future, such materials may begin to be used in cars or in aircraft, where the emphasis on light and strong materials is driven by the need to reduce weight, improve fuel efficiency and enhance environmental performance.

"There have been some studies to suggest that graphene-containing composites offer improved resistance to fatigue, but until now, nobody had measured the fatigue behaviour of the underlying material," he says. "Our goal in doing this was to get at that fundamental understanding so that in the future, we'll be able to design composites that work even better."


Explore further

Researchers use chicken poop to dope graphene to make a point

More information: Teng Cui et al, Fatigue of graphene, Nature Materials (2020). DOI: 10.1038/s41563-019-0586-y
Journal information: Nature Materials

Citation: Stress test reveals graphene won't crack under pressure (2020, January 29) retrieved 6 April 2020 from https://phys.org/news/2020-01-stress-reveals-graphene-wont-pressure.html
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.
445 shares

Feedback to editors

User comments