Study explains strength gap between graphene, carbon fiber
Carbon fiber, a pillar of strength in materials manufacturing for decades, isn't as good as it could be, but there are ways to improve it, according to Rice University scientists.
They found the polymer chains that make up a common carbon fiber are prone to misalign during manufacture, a defect the researchers compared with a faulty zipper that weakens the product.
The Rice lab of theoretical physicist Boris Yakobson set out to analyze these overlooked defects and suggest how they might be curtailed. The lab's work appears this month in Advanced Materials.
Carbon fibers were fabricated as long ago as the 19th century, when Thomas Edison made them as filaments for his prototype lightbulbs; but serious industrial development didn't begin until the late '50s. They are strong, flexible, conductive, heat-resistant and chemically inert, and have been used in tennis rackets, bicycle frames and aircraft, among many other products. They can also be spun into yarn for light and tough fabrics.
"Although well-established and mature, the field of carbon fibers has largely remained inert to using and benefiting from the intensive theoretical development in the 'young' field of low-dimensional nanocarbon," said Evgeni Penev, a research scientist in Yakobson's lab and co-author of the paper.
The Rice team built computer models to deduce the occurrence of defects in the most widely used carbon fiber manufacturing process, which involves heating polyacrylonitrile (PAN). At 1,500 degrees Celsius, the heat burns off all but the strongly bound carbon atoms, ultimately turning them into rudimentary graphene nanoribbons aligned in a way that prevents the ribbons from easily zipping into graphene's familiar honeycomb lattice.
Yakobson said the idea of this "misfusion" in fiber synthesis came to him while reading a biology paper about D-loops in RNA transcription. It occurred to him that such defects would be unavoidable in PAN-made carbon fiber as well. "It took a lot of work after that to determine their place and mechanical consequences in the fiber context," he said.
Molecular dynamics simulations revealed misfusion buckled the individual polymer chains and formed D-loops. These loops became the primary limiting factor of carbon fiber's vaunted strength; they reduced it by up to a factor of four and effectively dropped the theoretical estimates of fiber strength closer to what has been observed experimentally, the researchers reported.
"To me, the most intriguing part was realizing that D-loop defects enable the possibility of very large Burgers vectors, which are almost impossible in 3-D materials and would have been an absurd idea to even consider," said Nitant Gupta, a Rice graduate student and the paper's lead author. Burgers vectors are a measure of the strength-influencing distortions caused by dislocations in a crystal lattice.
To their surprise, the researchers discovered that when the PAN chains were misaligned with the fiber axis, the strength of the fiber increased despite the presence of D-loops.
They also determined D-loops might be prevented entirely by starting with graphene nanoribbons rather than PAN. Because D-loops are the most likely places for cracks to start, according to simulations, eliminating as many of them as possible would benefit the fiber's strength.
"Aside from specifics, we like to see this work as an attempt to cross-fertilize these fields at an atomistic-modeling level," Penev said. "We hope this will provide added value to those working in the field and eventually to a much broader audience."
More information: Nitant Gupta et al, Carbonization with Misfusion: Fundamental Limits of Carbon-Fiber Strength Revisited, Advanced Materials (2016). DOI: 10.1002/adma.201603009
Journal information: Advanced Materials