Universal ink for microcontact printing

Jun 01, 2006

"Printing" on the micrometer scale is the technology of the future for the production of the electronic components used for such things as flat-screen monitors or (bio)sensors.

Metal surfaces a few tens of square centimeters in size can already be structured without much experimental difficulty through a combination of microcontact printing and an etching process. Researchers are currently working to develop a simple production technology that is also broadly applicable for large surfaces. A team at Philips Research in Eindhoven in the Netherlands has now developed a universally applicable “ink” for microcontact printing.

The first step in microcontact printing is the production of an elastomeric malleable stamp by means of a mold. The stamp is then loaded with a special “ink” and is pressed onto the metal surface to be printed. The ink sticks to the metal surface and reproduces the microstructure of the stamp in a monomolecular layer. This monolayer acts as a corrosion-resistant mask in the subsequent etching process: the coated areas are not affected, whereas the metal in the uncoated areas is etched away, transferring the microstructure to the metal.

Precious and coinage metals are both used, as are materials with oxidic surfaces, such as silicon and aluminum. Each type of surface requires a different type of ink to stick to it: precious and coinage metals need ink molecules that can be bound by means of a metal–sulfur bond. Oxidic surfaces bind molecules with an acid functionality, such as carboxylic acids or phosphonic acids. Substrates that have different types of metals on their surface are thus not easy to structure.

Also, identical structures cannot be transferred onto different substrates with the same stamp, because once loaded, the stamp cannot be “washed” off and loaded with a different ink easily—and production of a new stamp is the most expensive part of the process.

The researchers led by Dirk Burdinski have now developed a universally applicable ink. It consists of a mixture of both types of ink, sulfur-containing octadecanethiol and octadecanephosphonic acid. When polydimethylsiloxane stamps are loaded with this ink, both types of metals can be structured.

The individual components of the ink are selectively transferred to their corresponding surface without interfering with each other. This universal ink is potentially also useful for the coating of microfluidic systems on diagnostic chips, as these often have inner wall structures made of different materials. Also electronic component blocks requiring good adherence of the protective coating to different components could thus first be homogenized at the surface, allowing for better sealing.

Citation: Dirk Burdinski, Universal Ink for Microcontact Printing, Angewandte Chemie International Edition, doi: 10.1002/anie.200600310

Source: Angewandte Chemie

Explore further: Taking great ideas from the lab to the fab

add to favorites email to friend print save as pdf

Related Stories

A material that most liquids won't wet

Jan 16, 2013

(Phys.org)—A nanoscale coating that's at least 95 percent air repels the broadest range of liquids of any material in its class, causing them to bounce off the treated surface, according to the University ...

How to corner the MEMS market

Apr 05, 2012

In the last decade, MEMS (microelectromechanical devices) have wrought revolutions in several industries: Arrays of micromirrors, for instance, enabled digital film projectors, and accelerometers like those ...

Recommended for you

Apple closes acquisition of Beats music

1 hour ago

Apple said Friday it closed its $3 billion deal for Beats, the high-end audio equipment and streaming music service, a tie-up that could allow the iPhone maker to reach new audiences.

Researchers jailbreak iOS 7.1.2

2 hours ago

Security researchers at the Georgia Tech Information Security Center (GTISC) have discovered a way to jailbreak current generation Apple iOS devices (e.g., iPhones and iPads) running the latest iOS software.

User comments : 0