Promising fire retardant results when clay nanofiller has space

Jul 07, 2011

(PhysOrg.com) -- If materials scientists accompanied their research with theme songs, a team from the National Institute of Standards and Technology and the University of Maryland might be tempted to choose the garage punk song "Don't Crowd Me"* as the anthem for the promising, but still experimental nanocomposite fire retardants they are studying.

That's because the collaborators have demonstrated that the more widely and uniformly dispersed nanoscale plates of clay are in a polymer, the more the nanocomposite material provides.

Writing in the journal Polymer,** the team reports that in tests of five specimens—each with the same amount of the nanoscale filler (5 percent by weight)—the sample with the most widely dispersed clay plates was far more resistant to igniting and burning than the specimen in which the plates mostly clustered in crowds. In fact, when the two were exposed to the same amount of heat for the same length of time, the sample with the best clay dispersion degraded far more slowly. Additionally, its reduction in mass was about a third less.

In the NIST/UMD experiments, the material of interest was a polymer—a type of polystyrene, used in packaging, insulation, plastic cutlery and many other products—imbued with nanometer scale plates of montmorillonite, a type of clay with a sandwich-like molecular structure. The combination can create a material with unique properties or properties superior to those achievable by each component—clay or polymer—on its own.

Polymer-montmorillonite nanocomposites have attracted much research and commercial interest over the last decade or so. Studies have suggested that how the clay plates disperse, stack or clump in polymers dictates the properties of the resultant material. However, the evidence—especially when it comes to the flammability properties of the nanocomposites—has been somewhat muddy.

Led by NIST guest researcher Takashi Kashiwagi, the NIST-UMD team subjected their clay-dispersion-varying samples to an exhaustive battery of characterization methods and flammability tests. Affording views from the nanoscopic to the microscopic, the array of measurements and flammability tests yielded a complete picture of how the nanoscale clay plates dispersed in the and how the resultant material responded when exposed to an influx of heat.

The researchers found that with better dispersion, clay plates entangle more easily when exposed to heat, thereby forming a network structure that is less likely to crack and leading to fewer gaps in the material. The result, they say, is a heat shield that slows the rate of degradation and reduces flammability. The NIST team, led by Rick Davis, is now exploring other approaches to reduce flammability, including the use of advanced and novel coating techniques.

Explore further: Two teams pave way for advances in 2D materials

More information:
* Keith Kessler, "Don't Crowd Me."
** M. Liu, X. Zhang, M. Zammarano, J.W. Gilman, R.D. Davis and T. Kashiwagi. Effect of Montmorillonite dispersion on flammability properties of poly(styrene-co-acrylonitrile) nanocomposites. Polymer. Vol. 52, Issue 14, June 22, 2011.

add to favorites email to friend print save as pdf

Related Stories

Nano-particle dispersion technique improves polymers

Aug 29, 2005

Supercritical fluid carbon dioxide used; melt properties provide monitor There is a lot of excitement about incorporating nano particles into polymers because of the ability to improve various properties with only a small per ...

Carbon nanotubes eliminate polymer manufacturing headache

Aug 14, 2004

Researchers at the National Institute of Standards and Technology (NIST) have discovered that the addition of carbon nanotubes to a common commercial polymer, polypropylene, leads to dramatic changes in how the molten polymer flows. This process elimin ...

Recommended for you

Two teams pave way for advances in 2D materials

2 hours ago

This month's headlines on two-dimensional polymers showed noteworthy headway. "2-D Polymer Crystals Confirmed At Last," said Chemical & Engineering News. "Engineers Make the World's First Verified, 2-Dimensional P ...

Nature inspires a greener way to make colorful plastics

20 hours ago

Long before humans figured out how to create colors, nature had already perfected the process—think stunning, bright butterfly wings of many different hues, for example. Now scientists are tapping into ...

New catalyst converts carbon dioxide to fuel

22 hours ago

Scientists from the University of Illinois at Chicago have synthesized a catalyst that improves their system for converting waste carbon dioxide into syngas, a precursor of gasoline and other energy-rich products, bringing ...

Bullet 'fingerprints' to help solve crimes

22 hours ago

Criminals don't just have to worry about their own fingerprints these days: because of a young forensic scientist at The University of Western Australia, they should also be very concerned about their bullets' ...

User comments : 0