Study proposes general A-site alloying strategy to prepare noble metal-occupied MAX phases
Researchers led by Prof. Huang Qing from the Ningbo Institute of Materials Technology and Engineering (NIMTE) of the Chinese Academy of Sciences, in collaboration with researchers from the Zhejiang Institute of Tianjin University and Linköping University, Sweden, have proposed a general A-site alloying strategy for the preparation of noble metal-occupied MAX phases.
The work is published in Matter.
MAX phases are a family of ternary layered transition metal carbides that have attracted significant attention as high-temperature structural materials. Researchers have gradually expanded the types of atoms in A-sites from traditional main group elements to include subgroup elements with an outer layer three-dimensional (3D) electronic structure. However, research on MAX phases with A-site elements having 4d/5d-orbital electronic structures has been limited.
Prof. Huang and colleagues delved into this obscure field and proposed a general A-site alloying strategy. This strategy enables the preparation of more than 100 MAX phases with noble metal-occupied elements in the A-site of the crystals due to the diversity of chemical composition and crystal structure of MAX phases.
Specifically, one or more of the six noble metals, i.e., ruthenium, rhodium, palladium, iridium, platinum, and gold, occupy the A atomic layers, with aluminum, gallium, indium, germanium, tin, and other solid solution A-site elements being randomly selected. Titanium, vanadium, and niobium are used as the M-site elements.
Noble metal-occupied MAX phases with different morphologies were synthesized by choosing the raw carbon powders.
Compared with commercial Pt/C, the Pt-occupied MAX phase produced in this study exhibited superior catalytic performance for the alkaline hydrogen evolution reaction, including lower overpotential, lower Tafel slope, higher mass activity, and better cyclic stability.
The noble metal-occupied MAX phases produced via general A-site alloying show broad application prospects in electrocatalysis and beyond.
More information: Huang Qing et al, A-site alloying-guided universal design of noble metal-based MAX phases, Matter (2024). DOI: 10.1016/j.matt.2023.12.006. www.cell.com/matter/fulltext/S2590-2385(23)00618-5