Combating sulphuric acid corrosion at wastewater plants

February 23, 2018, Graz University of Technology
Microbial induced concrete corrosion (MICC) causes massive damage to wastewater plants. Austrian Researchers from Graz present a new solution against the sulphuric acid attack. Credit: © TU Graz

Writing in Water Research, Austrian researchers from TU Graz and the University of Graz discuss new materials that prevent damage from microbial induced concrete corrosion.

Wastewater systems are integral to infrastructure in every community. In an ideal world, they operate smoothly and are long-lasting. But biogenic transformation processes in sewage and water treatment systems are a "natural enemy" of conventional plants, frequently causing damage to concrete and metal elements that is expensive to repair. As a result, it is not uncommon for systems to have a lifespan of under ten years, before they need to be refurbished or individual components replaced. Toxic gases released during biogenic processes, such as , also pose a significant health risk, causing a range of symptoms from irritation to respiratory failure and death.

Writing in the journal Water Research, an interdisciplinary group of researchers from TU Graz and the University of Graz has outlined strategies aimed at preventing what is termed microbial induced concrete corrosion (MICC).

Microbial induced concrete corrosion: turning a blind eye not the answer

Cyrill Grengg of the Institute of Applied Geosciences at TU Graz explained: "MICC often corrodes the conventional types of concrete used in at a rate of a centimetre or more per year. Accordingly, the concrete elements can be destroyed in a matter of only a few years, causing significant damage to wastewater systems." According to the researchers, there is often a lack of awareness of these processes and the resulting threat to wastewater infrastructure and human health. "Closing the manhole covers and looking the other way is not the answer," Grengg added. In Germany alone, the economic impact of wastewater system repairs is put at around EUR 450 million per year. Although no data are currently available for Austria, the costs can be extrapolated and also applied to other European countries.

Microbial induced acid corrosion (MICC) in wastewater treatment facilities results from a sequence of biogenic sulphate reduction reactions, followed by reoxidation. Initially, sulphate in pressure pipelines or standing wastewater is reduced by bacteria under anaerobic – or oxygen-free – conditions, forming hydrogen sulphide. This pungent, highly poisonous gas escapes into the sewer air and diffuses into sewer pipes and manholes. There reoxidation by autotrophic bacteria takes place on concrete walls that do not even come into contact with wastewater. These microorganisms produce sulphuric acid which reacts with concrete construction elements. As Günther Koraimann of the Institute of Molecular Biosciences at the University of Graz, who has studied these processes in detail, explains: "This leads to the vigorous formation of a biofilm on the surface of the concrete, a reduction of the pH value to below two, in other words highly acidic, and extensive formation of new minerals, mainly in the form of gypsum. The combination of these processes results in the rapid destruction of the concrete."

Holistic solution

The Graz-based scientists worked on a holistic solution using an interdisciplinary research approach. In-depth research into the microstructural and microbiological processes was followed by the development of new MICC-resistant materials in close collaboration with the Institute of Construction and Building Materials at TU Darmstadt. In this context, geopolymer concrete proved to be particularly well suited to withstand acid corrosion. When developing this building material, resistance to acid was an extremely desirable property, as were highly antibacteriostatic surfaces, on which the research team made significant advances – microorganisms that trigger the initial oxidation process are unable to settle on such surfaces in the first place. In turn, this prevents the formation of sulphuric acid. Florian Mittermayr of the Institute of Technology and Testing of Construction Materials at TU Graz commented: "We achieved some very promising results with materials that have a far greater lifespan than conventional types of concrete. Use of these long-lasting materials would allow operators to refurbish damaged wastewater systems, significantly extending their service life and reducing the financial burden on local government and wastewater associations." The researchers published their latest findings on MICC prevention in the current issue of the journal Water Research 134 (2018) 341—352: "Advances in concrete for sewer systems affected by microbial induced concrete corrosion: A review."

The Austrian province of Styria provided financial backing for the research, and is dedicated to raising awareness of this global problem among Styrian local authorities and regional wastewater associations.

Explore further: How to tell when a sewage pipe needs repair—before it bursts

More information: Cyrill Grengg et al. Advances in concrete materials for sewer systems affected by microbial induced concrete corrosion: A review, Water Research (2018). DOI: 10.1016/j.watres.2018.01.043

Related Stories

Tracking wastewater's path to wells, groundwater

January 24, 2018

We often "flush it and forget it" when it comes to waste from toilets and sinks. However, it's important to be able to track this wastewater to ensure it doesn't end up in unwanted places. A group of Canadian scientists has ...

Recommended for you

Scientists capture sounds of volcanic thunder

March 15, 2018

Researchers report in a new study that they've documented rumblings of volcanic thunder for the first time, a feat considered nearly impossible by many volcanologists.


Please sign in to add a comment. Registration is free, and takes less than a minute. Read more

Click here to reset your password.
Sign in to get notified via email when new comments are made.