Crystal structure of metals can change at linear defects, which should affect the properties of the materials

September 11, 2015, Max Planck Society
Structural change in steel: Scientists at the Max-Planck-Institut für Eisenforschung use images from a transmission electron microscope (grey) to make linear defects in an alloy of iron (Fe) and manganese (Mn) visible. Atom probe tomography shows them the distribution of the iron (blue) and manganese atoms (green). They have put green iso-surfaces into the image where the concentration of the manganese atoms is 12.5 percent. In the superimposed images, the researchers can see that the manganese atoms accumulate along the linear defects; the crystal structure which forms there is different to the surrounding material. Credit: M. Kuzmina/MPI für Eisenforschung

Steel has already been around for roughly 3000 years and in several thousand variations today - yet it is always good for a surprise. Scientists at the Max-Planck-Institut für Eisenforschung in Düsseldorf have now made a discovery in manganese steel which is thought to affect the properties of the material for good and bad. They have found out that the alloy forms a different crystal structure at linear defects than is typical for the material. The individual crystal grains of which any metal is composed can be considered as a stack of individual atomic layers. Linear defects, or more precisely edge dislocations, occur when a layer remains incomplete so that the layers above and below it must take a step. As the length of the linear defects in a cubic metre of steel can add up to one light year, the discovery ought to have great practical significance since the structure of a steel depends on, among other factors, how malleable, rigid and ductile it is – properties which material scientists want to continuously optimize.

Dislocations can save lives. This stems from the fact that the one-dimensional defects in a metal play an important role when the material deforms: for example, when a car body panel crumples in an accident, thus absorbing a large part of the impact energy and hopefully protecting the passengers from injury. In such a case, the dislocations act as nano-hinges along which a metal bends. The fact that the differs from the structure immediately around the linear defect should therefore also affect how the metal deforms. In the worst case, it tears rather than deforms. "We don't yet know what effect the spatially confined chemical and structural states in the material have on its properties," says Dierk Raabe, Director at the Max-Planck-Institut für Eisenforschung and head of the study in which the deviationists in the microstructure have just come to light.

"We stumbled across the states more by chance," says Dierk Raabe. He and his team had been investigating the micro- and nano-structure of a particularly rigid and ductile manganese steel which is strengthened with the aid of nanoparticles and is used in the landing gear of large aircraft, for example. They analysed this material with the aid of atom probe tomography. The analysis involves a sample being vaporized atom by atom with short pulses of an electric voltage. From the time-of-flight to a detector it is possible to determine to which element the vaporized detached atom belongs; its position in the sample can be determined from the location where the atom impinges on the detector.

The researchers found chains of manganese-rich nano-beads in the steel
"We noticed that the concentration of the manganese increased along specific lines after we had heated the material," explains Dirk Ponge, who made important contributions to the study. The fine tubes in which the manganese collects are only two nanometres wide. And this happens not along the whole length, but more in the form of a chain of manganese-rich nano-beads.

In order to accommodate the larger number of manganese atoms in these minute areas, the crystal structure of the material must change. Iron and normally sit at the corners and centers of a cubic unit cell, the smallest structural unit. The researchers call this a body-centred cubic or martensite structure. The manganese concentration in the chain of nano-beads corresponds to an arrangement in which the atoms are located on each face and corner of the unit cell, in technical terms, a face-centred cubic or austenite structure.

Previously, material scientists only knew such deviations from the regular crystal structure of a metal in two-dimensional form, i.e. from the boundaries of the individual crystal grains which form a material. But why did they find filigree austenite structures in the interior of individual martensite crystal grains? "When we saw that the manganese accumulated in thin tubes, we had the idea there could be spatially confined chemical and structural states along linear defects," says Dirk Ponge.

The different crystal structure at the defect helps to save energy
In order to be certain, he and his colleagues first scanned an iron-manganese sample in a transmission electron microscope, which makes linear defects clearly visible. They then mapped the distribution of the atoms in the sample again with the aid of . And on the superimposed images from both methods they actually did find how the manganese-rich nano-beads arrange themselves precisely along the linear defects.

The fact that the atoms arrange themselves differently from the remaining crystal precisely along the dislocations is also suggested by an explanation of the observation: "The stress is particularly high at the dislocations," says Dirk Ponge. "The material can apparently reduce stress and thus assume an energetically more favourable state by forming a crystal structure there which would be energetically less favourable otherwise." On the basis of this finding, the Düsseldorf-based researchers extended a key formula that material scientists use to calculate which structure a material favours under which conditions at such structural defects.

Can a Damascus steel forge itself?
The researchers had first to mobilize the atoms with heat so that the atoms could assume the structure which is energetically more favourable there, directly at the dislocation, and only there. "This doesn't mean that the spatially confined chemical and structural states form only when heat is applied, however," says Dierk Raabe. These states can therefore probably not only be found in the cylinders of a motor, the blades of a turbine or other that are permanently subjected to great heat. "Small atoms, such as those of carbon, are much more mobile than those of manganese," explains Dierk Raabe. "We therefore must assume that we will find the spatially confined states in carbon containing car body steel panels as well."

The researchers now want to investigate what effect the local structural change has on the properties of a material. "Our findings may help to explain an already known behaviour of metals – the fact, for instance, that metals become brittle when they corrode and absorb hydrogen," says Dierk Raabe.

However, it's not always bad news when the crystal structure at linear defects steps out of line. "Maybe we can bring about these spatially confined states intentionally in order to develop a nano-Damascus steel that forges itself," says the Max Planck Director. Damascus steel received its name because it came to Europe via Damascus. Expert craftsmen in the Orient forged a hard, yet brittle, and a ductile, yet soft steel into a composite material which is hard, but does not break easily. In future, a simple way may be found to combine these actually incompatible properties, if dislocations could be used to help provide a structure. This would open up completely new possibilities for the steel industry to optimize a material for a special application in an even more targeted way.

Explore further: Thin film produces new chemistry in 'nanoreactor'

More information: "Linear Complexions: Confined Chemical and Structural States at Dislocations," Science, 4. September 2015. DOI: 10.1126/science.aab2633

Related Stories

Thin film produces new chemistry in 'nanoreactor'

November 19, 2014

Physicists of the University of Groningen and the FOM Foundation, led by professor Beatriz Noheda, have discovered a new manganese compound that is produced by tension in the crystal structure of terbium manganese oxide. ...

NCNR neutrons highlight possible battery candidate

May 21, 2014

Analysis of a manganese-based crystal by scientists at the National Institute of Standards and Technology (NIST) and the Massachusetts Institute of Technology (MIT) has produced the first clear picture of its molecular structure. ...

2-D materials' crystalline defects key to new properties

September 24, 2014

Understanding how atoms "glide" and "climb" on the surface of 2D crystals like tungsten disulphide may pave the way for researchers to develop materials with unusual or unique characteristics, according to an international ...

Materials science: Perfecting the defect

May 3, 2012

Strong metals have a tendency to be less ductile — unless the metal happens to be a peculiar form of copper known as nanotwinned copper. The crystal structure of nanotwinned copper exhibits many closely-spaced interruptions ...

Recommended for you

Understanding insulators with conducting edges

January 16, 2019

Insulators that are conducting at their edges hold promise for interesting technological applications. However, until now their characteristics have not been fully understood. Physicists at Goethe University have now modelled ...

Mechanism helps explain the ear's exquisite sensitivity

January 16, 2019

The human ear, like those of other mammals, is so extraordinarily sensitive that it can detect sound-wave-induced vibrations of the eardrum that move by less than the width of an atom. Now, researchers at MIT have discovered ...

10 comments

Adjust slider to filter visible comments by rank

Display comments: newest first

adave
3.4 / 5 (5) Sep 11, 2015
Wootz steel was a lost art until rediscovered by Mr. Pendray. Verhoeven and A. Pendray described one method of making wootz steel that makes a damascus composite structure from a casting. Alfred Pendray has been casting and forging wootz knives since 1982. An article based on their published research can be found in the Scientific American. Other methods involve preventing carbon migration in the composite of a mechanical damascus steel made of a welded and folded stack of different alloy bars. The advantage is that you can have very hard and very tough properties in the same piece of low alloy and low cost steel. The lost method of Masamune and his 10 first generation students Sadamune and unrelated Muramasa made a fine structured composite that out performed all other swords of their time. They were said to cut all day. The edge at less than a 20 deg. angle did not degrade and stayed sharp. The edge held up in the sunlight was not visible. Dull spots are bright, reflecting light.
RealScience
2.3 / 5 (3) Sep 12, 2015
@adave - I read that Sci Am article years ago and have tried to find it several times since then - do you have a link?
adave
3.7 / 5 (3) Sep 12, 2015
adave
3 / 5 (2) Sep 12, 2015
Wootz melts at cast iron temps 2400 deg F. Oddly expanding as it cools. See the ingot photo in History of Metallography by Cyril Smith. The pillar of Delhi is said to be cast wootz. A Glossary of the Construction, Decoration and Use of Arms and Armor: in All Countries and in All Times by George C. Stone has further information.
RealScience
not rated yet Sep 13, 2015
@adave - thank you for the link!

A few years ago I was discussing 'Damascus steel' with two friends who are blacksmiths, and both were familiar with the laminate-and-repeatedly-fold technique ('welded') for making 'Swedish steel' with hundreds of layers of hard and soft steel, but not with the 'Damascus' technique of starting with a wootz cake with an inter-dendritic pattern of carbon-attracting impurities.

I found quite a few articles (enough to convince them that the true 'Damascus steel' was NOT made by folding), but I could not find this article, which I consider the best one.

One of the blacksmith's has since found a supplier of 'wootz' cakes and has made himself a beautiful knife therefrom, but it is still not as good as the originals... perhaps the details in this article will allow him to finally make true 'Damascus steel' blades, so thank you again for the link!
docile
Sep 13, 2015
This comment has been removed by a moderator.
docile
Sep 13, 2015
This comment has been removed by a moderator.
RealScience
1 / 5 (1) Sep 13, 2015
Well if it isn't lajib and hewewa rating the comments in this thread

Funny how they were created one minute apart and have never made any comment in the two months they have existed.
Funny how they downvote everyone in this thread except docile, and give docile's comments five stars. Oh look, they've given other comments by docile five stars.

I smell sock puppets!

But what I don't get is why this thread??? adave's comments were factual, useful and well written, and were not on a controversial subject, so it must be some sort of grudge from a previous thread.
It is a pity that people take comments or commenters so personally that they hold grudges and grade comment according to who wrote them rather than on what the comments themselves say.

I'll set an example and give docile's first comment a 5 because it is a good comment, in spite of the suspicion that docile is upvoting himself and downvoting adave and me.

docile
Sep 13, 2015
This comment has been removed by a moderator.
RealScience
not rated yet Sep 13, 2015
@docile - I wasn't sure that lajib and hewewa were YOUR sock puppets, just that they are sock puppets. (But I admit that I was a bit suspicious - the only other commenter I've seen either one upvote is RealityCheck, and that was a while ago).

Thank you for answering, and I apologize for voicing suspicion without solid evidence.

Please sign in to add a comment. Registration is free, and takes less than a minute. Read more

Click here to reset your password.
Sign in to get notified via email when new comments are made.