Creating high-quality, thick graphite films

New study introduces the best graphite films
Figure 1. Illustration of graphite growth on an rough substrate, on which disorders, namely grain boundaries, between single crystalline graphite islands nucleated on different flat terraces are inevitable. Credit: UNIST

High-quality graphite has excellent mechanical strength, thermal stability, high flexibility and very high in-plane thermal and electric conductivities, and therefore it is one of most important advanced materials used in many applications, including light thermal conductors in cell phones. For example, a specific type of graphite, Highly Ordered Pyrolytic Graphite (HOPG), is one of the most frequently used lab materials.

These excellent properties originate from the layered structure of graphite, where the strong covalent binding between in a layer contribute to the excellent mechanical properties. Thermal and electric conductivities and the very weak interaction between graphene layers leads to the high flexibility of graphite.

Although graphite has been known in its natural form for more than 1,000 years and its artificial synthesis has been explored for more than 100 years, the quality of graphite samples, either natural ones or synthesized ones, are far from ideal. The size of the largest single crystalline graphite domains in graphitic materials is generally less than 1 mm, which is in sharp contrast to the size of many crystals, such as quartz and silicon single crystals that may reach meter scale.

The very small size of single crystalline graphite is due to the between graphite layers, where the flatness of a graphene layer is hard to maintain during the . Therefore graphite can be easily broken into a few single crystals with disordered (see figure 1).

To solve this critical issue, Distinguished Professor of Ulsan National Institute of Science and Technology (UNIST) and his collaborators, Professor Kaihui Liu, Professor Enge Wang of Peking University and others have proposed a strategy to synthesize single-crystalline graphite films orders of magnitude large, up to inch scale. In their approach, single crystalline Ni foils are used as a substrate and caron atoms are supplied from the back side of the Ni foils through an isothermal dissolution-diffusion-precipitation process (see figure 2).

Instead of using gas phase carton source, they choose solid carbon materials to feed the graphite growth. The new strategy creates ~1 inch single crystalline graphite films of 35 μm thick, or more than 100,000 graphene layers, within a few days. The single crystalline graphite has the recorded thermal conductivity of ~2,880 Wm-1K-1, negligible impurity contents and smallest layer distances compared with all available graphite samples.

New study introduces the best graphite films
Figure 2. (a) The mechanism of single crystalline graphite growth on a ultraflat single crystalline Ni foil: (i) carbon atoms of the solid carbon source dissolve into the single crystalline Ni; (ii) and the dissolved carbon atoms transport through the Ni foil to another side to forma graphene flakes; (iii) graphene flakes continuously merge into single crystalline graphene films and (iv) finally thick graphite films are formed on the single crystalline Ni substrate. (b) part of the experimentally grown inch-sized single crystalline graphite, on which the wrinkles formed during the cooling of the sample can be seen. (c) the ultra-flat graphite films formed by etching the substrate after growth. Credit: UNIST

"This success really on a few critical issues of the experimental design: (1) the successful synthesis of large size single crystalline Ni films serves as an ultra-flat substrate and thus the disorders in the synthesized graphite can be avoided; (2) the isothermal growth of 100,000 graphene layers over ~ 100 hours allows every graphene layer be synthesized under exact same chemical environment and temperature thus ensure the uniformity of the quality; (3) continuous carbon feeding through the back side of the Ni foil allows the contiguous growth of in a very large growth rate, ~ one layer per five seconds," Professor Ding explained.

The findings of this research were published in the October 2022 issue of Nature Nanotechnology.

More information: Zhibin Zhang et al, Continuous epitaxy of single-crystal graphite films by isothermal carbon diffusion through nickel, Nature Nanotechnology (2022). DOI: 10.1038/s41565-022-01230-0

Journal information: Nature Nanotechnology

Citation: Creating high-quality, thick graphite films (2022, November 4) retrieved 17 April 2024 from
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.

Explore further

Graphene is 3-D as well as 2-D


Feedback to editors