Intermetallic palladium-zinc alloy: A corrosion-resistant, highly active electrocatalyst

Intermetallic palladium-zinc alloy: a corrosion-resistant, highly active electrocatalyst
The crystal structure of the intermetallic i-PdZn alloy allows Zn to be retained at the core, surrounded by a protective shell of Pd atoms. This gives the i-PdZn better corrosion resistance when immersed in highly alkaline solutions, unlike the substitutional alloy s-PdZn, where random replacement of Pd atoms by Zn in the crystal structure allows the Zn to leach out quickly. Credit: Hiroshi Inoue, Osaka Metropolitan University

Osaka Metropolitan University researchers have created intermetallic alloy nanoparticles of palladium and zinc with an alternating arrangement of zinc and palladium atoms. The intermetallic alloy is more corrosion-resistant than substitutional alloys while retaining the electrocatalytic properties of both metals, which could be useful for developing new non-precious metal electrocatalysts.

Palladium—a precious —is attracting attention as a fuel cell , which requires metals with high electrocatalytic activity. Because of the high cost of palladium, creating a palladium- alloy should improve while reducing costs. In addition, is important for potential electrocatalyst materials because catalytic reactions use extremely corrosive alkaline aqueous solutions that degrade metal electrocatalysts and lower their efficiency over time.

A research group led by Professor Hiroshi Inoue, Associate Professor Eiji Higuchi, and Associate Professor Masanobu Chiku of the Graduate School of Engineering, Osaka Metropolitan University, has found a promising intermetallic alloy of palladium and zinc (i-PdZn). The intermetallic alloy has a precisely arranged atomic structure consisting of equal amounts of alternating palladium and zinc atoms. This makes the i-PdZn highly resistant to corrosion in alkaline aqueous solutions.

Metal alloys can be substitutional or intermetallic. In a substitutional palladium-zinc alloy, zinc atoms replace half of the palladium atoms at random, whereas palladium and zinc atoms in the new intermetallic alloy i-PdZn are arranged in an alternating fashion so that each zinc atom is surrounded by palladium atoms and vice versa.

When both the i-PdZn and the substitutional palladium-zinc alloy were immersed in an aqueous alkaline solution, the researchers found that most of the zinc atoms leached out of the substitutional alloy within a few minutes. However, the regular arrangement of palladium and zinc atoms in the i-PdZn effectively prevented the zinc atoms in the middle of the alloy from leaching out. This created a protective skeletal palladium shell around the outside of the alloy, giving the i-PdZn a much higher corrosion resistance.

Furthermore, when used as an electrocatalyst to generate, the i-PdZn exhibited a peak ethanol oxidation activity approximately 5.1 times as high as that of pure palladium. This was due to both the electronic properties of the alloy's core, and the larger surface area created by the skeletal palladium shell in the aqueous alkaline solution.

"The unique properties of intermetallic alloys that make them good catalysts were previously known, but now we have shown that the dissolution of zinc is greatly suppressed in our intermetallic -zinc alloy, which makes it much more corrosion-resistant than the substitutional alloy," Professor Inoue concluded. "We believe that these results may provide clues for the development of non-precious metal electrocatalysts, for which corrosion resistance is an issue."

The research results were published online on July 23, 2022, in Research on Chemical Intermediates.

More information: Nguyen Trung Kien et al, Activity and durability of intermetallic PdZn electrocatalyst for ethanol oxidation reaction, Research on Chemical Intermediates (2022). DOI: 10.1007/s11164-022-04780-z

Provided by Osaka Metropolitan University

Citation: Intermetallic palladium-zinc alloy: A corrosion-resistant, highly active electrocatalyst (2022, October 18) retrieved 28 May 2023 from
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.

Explore further

Tuning exact ratios of two metals in a catalyst may enable new directions in catalysis science


Feedback to editors