Synthesis of diamond-like carbon nanofiber film

Synthesis of diamond-like carbon nanofiber film
Figure 1. Field Emission-Scanning Electron Microscope images of copper nanoparticles and of the synthesized diamond-like carbon fiber film, and a High-Resolution transmission electron microscope image of a single nanofiber. Credit: Professor Rodney S. Ruoff (IBS CMCM, UNIST

An international team of researchers, led by Distinguished Professor Rodney S. Ruoff (Department of Chemistry) from the Center for Multidimensional Carbon Materials (CMCM), within the Institute for Basic Science (IBS) at UNIST, has synthesized a film composed of densely packed diamond-like carbon nanofibers. As described in a recent article published in the journal ACS Nano, the researchers noted that the new carbon material has a high concentration of tetravalently-bonded carbons (the diamond-like nanofibers have many C atoms with four other atoms bonded to them; this is also referred to as "sp3-bonded carbon").

"The diamond-like carbon films were synthesized by heating copper nanoparticles of few nanometers in diameter on a substrate, in acetylene and hydrogen gasses," says Kee Han Lee. "The synthesized fibers were highly dense and formed a film. These densely packed nanofibers could also be separated into a powder form which could potentially broaden their applications."

In this study, the team was able to identify parameters influencing the packing density of the nanofibers namely the hydrogen gas concentration and the copper nanoparticle catalyst size. The packing density could be significantly increased by adjusting these parameters, which led to the formation of a buckled film.

Various techniques such as X-ray photoelectron spectroscopy, solid-state nuclear magnetic resonance, elemental analysis, and Raman spectroscopy elemental composition and chemical bonding structure in these diamond-like nanofibers, and it was found that sp3-bonded (sp3: sp2 carbon atom ratio of about 2) predominate (sp2-bonded C atoms are attached to three other atoms rather than four—like in graphene and graphite—whereas in diamond, all C are "sp3-bonded"). Hydrogen content within the nanofibers of about 25−50 atomic% was determined using Raman spectroscopy and elemental analysis.

"With its high sp3-carbon content, this material is different from other vapor grown carbon nanofibers including nanotubes, which are mostly composed of stacked graphene layers, and carbon nanocoils that have an sp3: sp2 carbon ratio of about 0.25," explains Sun Hwa Lee.

The (1.2 ± 0.1 × 106 Ω cm—it is electrically insulating), density (2.5 ± 0.2 g cm-3; the density of diamond is 3.5 g cm-3), surface area (28 ± 0.7 m2 g-1), chemical inertness, and wettability towards various liquids, were determined. These properties were similar or "better" than most diamond-like carbon films reported, but the mechanical properties of this diamond-like carbon nanofiber film were found to be entirely different than conventional, continuous, diamond-like carbon , because it is composed of nanofibers.

"We discovered a new form of carbon, and one might expect our work to inspire others to now also study further along this research path," said Distinguished Professor Ruoff. "We do of new carbon materials among other things, and we are interested in eventually achieving pure diamond fibers, along with further studies of this type of diamond-like nanofiber."

More information: Kee Han Lee et al. Synthesis of Diamond-Like Carbon Nanofiber Films, ACS Nano (2020). DOI: 10.1021/acsnano.0c05810

Journal information: ACS Nano

Citation: Synthesis of diamond-like carbon nanofiber film (2020, November 4) retrieved 24 April 2024 from
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.

Explore further

New method allows direct conversion of carbon fibers and nanotubes into diamond fibers


Feedback to editors