A new carbon material with Na storage capacity over 400mAh/g

A new carbon material with Na storage capacity over 400mAh/g
(a) XRD pattern of the as-prepared sample indexed with amorphous and graphitized peaks. (b) Raman spectra of D, G, D+D'', 2D, D+G and 2D' bands. Credit: Science China Press

Developing high-capacity carbon anode materials can further improve the energy density of sodium-ion batteries (NIBs). Recently, researchers from the Institute of Physics, Chinese Academy of Sciences (IOP-CAS), reported a high-capacity carbon anode (~400 mAh g-1) for NIBs. The results are published in Science Bulletin.

Since 2010, sodium-ion batteries (NIBs) have been intensively investigated because of their cost and resource advantages and possible applications in large-scale energy storage systems. However, the energy density of current NIBs remains a serious challenge, hindering large-scale commercial applications. Hard carbon is one of the most promising anodes in the early commercial NIBs for high capacity (~330 mAh g-1), good cycling stability, high initial Coulombic efficiency, reasonable cost, and the natural abundance of precursor materials.

Although extensive efforts have been devoted to the development of high-performance materials, a consistent behavour in the discharge-charge curve is often presented with two distinct regions: a slope region above ~0.1 V and a plateau region below ~0.1 V. Usually, the plateau region exhibits a higher capacity than that of the slope region, and a high-capacity carbon anode often shows a large proportion of the plateau capacity, which could further increase the energy density of a full cell in terms of the average voltage to some extent. Therefore, designing and discovering a carbon anode with a large proportion of the plateau capacity can be a potential approach to increase the energy density of NIBs.

Recently, the team of Prof. Yong-Sheng Hu at the Institute of Physics, Chinese Academy of Sciences (IOP-CAS) reported a bi-honeycomb-like architecture carbon material by carbonizing a kind of charcoal in a high-temperature graphite furnace at 1900 °C. This carbon anode shows a high capacity of ~ 400 mAh g-1, which is higher than the ~ 330 mAh g-1 capacity of current hard carbon materials. About 85 percent (> 330 mAh g-1) of its total is derived from the long low-potential plateau below ~ 0.1 V, which differs from the curves of typical hard carbon materials of NIBs. When coupled with air-stable Na0.9Cu0.22Fe0.30Mn0.48O2 layered cathode, a high energy density of ~240 Wh kg-1 was obtained with good rate capability and cycling stability. The discovery of this promising is expected to draw further research toward high- NIBs for large-scale electrical energy storage.

  • A new carbon material with Na storage capacity over 400mAh/g
    Electrochemical properties of this anode in half cells. (a) Galvanostatic discharge-charge curves, (b) CV curves, (c) Cycling performance and (d) Rate capability. Credit: Science China Press
  • A new carbon material with Na storage capacity over 400mAh/g
    (a) Schematic illustration of charge-discharge voltage profiles of the carbon anode and Na0.9Cu0.22Fe0.30Mn0.48O2 cathode, respectively. Electrochemical performance of the carbon anode//Na0.9Cu0.22Fe0.30Mn0.48O2 the full cell, (b) Charge-discharge curves, (c) Rate capability and (d) Cycling performance. Credit: Science China Press

More information: Chenglong Zhao et al, High-temperature treatment induced carbon anode with ultrahigh Na storage capacity at low-voltage plateau, Science Bulletin (2018). DOI: 10.1016/j.scib.2018.07.018

Citation: A new carbon material with Na storage capacity over 400mAh/g (2018, September 20) retrieved 28 March 2024 from https://phys.org/news/2018-09-carbon-material-na-storage-capacity.html
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.