Fig: (a) Preparation of white light-emitting paste material by mixing solid dyes of green color (Alq3) and orange (rubrene) in a room temperature OPV iquid. (b) White light-emission of characters written with a ballpoint pen (365nm UV irradiation). (c) Large area coating emits white light on area of 5 x 5 cm2 (365nm UV irradiation). (d) 375nm UV-LED light-emitting photograph. (Left) Without coating with white light-emitting paste and (right) with coating.

A Japanese research team headed by Dr. Takashi Nakanishi of the National Institute for Materials Science developed a nonvolatile liquid material which emits white light at room temperature.

Because account for about 20% of all electric power consumption, and technological improvements are desired in order to reduce emissions of (GHG). In particular, high expectations are placed on organic materials which emit white light as a material for next-generation lighting, replacing today’s incandescent light bulbs and fluorescent tubes. Although the organic materials which have been developed to date display a white light-emitting property when dispersed in a solution, the molecules tend to aggregate when the solution is coated on a substrate and the solvent is evaporated. This problem is the reason why these materials cannot fully demonstrate their intrinsic white-light emitting performance. Furthermore, from the viewpoint of the manufacturing process, an which can be prepared by a simple method, without use of volatile organic solvents, achieving high brightness, homogeneous white light-emission, had been desired.

Dr. Nakanishi’s team developed a liquid material with blue light fluorescence which is nonvolatile, has a melting point of approximately -45°C, and solves the problem of molecule aggregation, by modifing highly flexible branched alkyl chains around the molecule that can emit fluorescence. This material is a liquid with a viscosity of approximately 1.0 Pa·s, which is similar to that of lubricating oil, and does not require use of a volatile organic solvent. It displays blue light emission with an absolute fluorescent quantum yield of approximately 50%. A white light-emitting paste material can also be prepared by mixing a small amount of luminescent dyes in solid powder in the liquid. Various materials which emit high brightness white light even when coated were successfully prepared, including printing of white light-emitting characters, large area coating, white light-emitting lights by coating on a UV-LED surface, and others.

This research achieved the development of materials which emit white light with high quality using only an extremely simple operation, namely, mixing of a small amount of solid dyes in the nonvolatile, blue light-emitting liquid. This liquid material can be coated on substrate surfaces with various shapes, and thus is expected to enable broad simplification of the manufacturing processes for lighting devices and other products. Because the emitted color can be controlled with a high brightness, and liquids that display full-color light emission can also be prepared easily, this material is expected to become a new light-emitting material for next-generation printable electronics.

More information: These research results were published in Angewandte Chemie International Edition (2012, 51, 3391-33), which is a publication of the German Chemical Society, and were also highlighted in Nature (2012, 484, 9).

Journal information: Angewandte Chemie International Edition , Nature