Researchers discover the cause of irradiation-induced instability in materials surfaces

A new discovery about the dynamic impact of individual energetic particles into a solid surface improves our ability to predict surface stability or instability of materials under irradiation over time.

The finding may lead to the design of improved for nuclear fission and fusion power plants, which must withstand constant irradiation over decades. It may also accelerate the advent of fusion power, which does not produce radioactivity.

Publishing in Nature Communications, Michael Aziz, Gene and Tracy Sykes Professor of Materials and Energy Technologies, and Michael Brenner, Glover Professor of Applied Mathematics and Applied Physics, both at the Harvard School of Engineering and Applied Sciences (SEAS), and colleagues developed a new rigorous that is "fed" the measured shape of the average crater resulting from the impact of an energetic particle.

The impacts, lasting a few trillionths of a second, are simulated using intensive . The theory then "up-scales" the cumulative effect of individual energetic particle impacts to predict evolution over thousands of seconds or longer.

"Our results illustrate how large-scale can be combined with rigorous mathematical analysis to yield precise predictions of new phenomena on length and timescales that would otherwise be computationally impossible," says Brenner.

The researchers were surprised to discover that stability/instability is not determined by the atoms that are blasted away, but instead by the atoms that are knocked around and re-settle nearby.

"Our discovery overturns a long-held paradigm about what causes surfaces to erupt into patterns under energetic particle bombardment. The blasting away of individual atoms from energetic particle impacts has long been thought to determine whether a surface is stable or unstable," says Aziz.

"The effect of atoms blasted away turns out to be so small that it is essentially irrelevant. The lion's share of the responsibility of what makes a surface stable or unstable under irradiation comes from the cumulative effect of the much more numerous atoms that are just knocked to a different place but not blasted away."

The team found that the cumulative effect of these displacements can be either ultra-smoothening, which may be useful for the surface treatment of surgical tools, or topographic pattern-forming instabilities, which can degrade materials. The outcome depends on the type of material, energetic particle, and irradiation conditions.

The discovery, while interesting in its own right, may also help to solve a mysterious degradation problem in tungsten plasma-facing reactor walls in prototype fusion reactors.

Tungsten is used for two reasons. First, it is inert to nuclear reactions that could arise from the bombardment by hydrogen and helium from the plasma. Additionally, "The material is so strongly bound that this bombardment does not lead to the blasting away of any tungsten atoms", says Aziz.

Yet, under some conditions the tungsten inexplicably becomes "foamy" or begins to degrade. Armed with insight from the new theory, the researchers considered the implications for foamy tungsten.

"Even under plasma conditions where no tungsten atoms are blasted away, they are indeed displaced to new positions," says Aziz. "We conjectured that the way the helium moves the tungsten atoms around is causing the instability. While more research will be needed to know for sure, we think we're finally in the position of being able to develop a predictive theory for tungsten by extending the one we have presented here for simpler materials."

Extending the study to more complex materials such as tungsten is an important future challenge, as it could lead to better design criteria for materials that must remain stable during exposure to irradiation, both for cleaner, safer fusion and for conventional fission reactors.

Aziz and his colleagues developed an experimental data set using ion beam irradiation of silicon because it is the simplest prototype material for such studies. Their theory was validated by detailed comparison of its predictions to their experimental results for surface ultra-smoothening, instabilities, and pattern formation in silicon.

"This could help solve a technical problem with nuclear , which holds promise for nuclear power without radioactivity" says Aziz.

Provided by Harvard University

Citation: Researchers discover the cause of irradiation-induced instability in materials surfaces (2011, April 12) retrieved 27 March 2023 from
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.