Naval research laboratory takes a close look at unique diamonds

March 23, 2010
The Wittelsbach-Graff diamond (31.06 ct, left) and the Hope diamond (45.52 ct, right) apparently were not cut from the same crystal, even though they share several similarities, such as strong red phosphorescence (bottom). Credit: Chip Clark, Smithsonian

The song says that "diamonds are a girl's best friend," but scientists at the Naval Research Laboratory are finding that diamonds are a researcher's best friend too.

NRL, which has been involved in pioneering work involving of diamond and the use of diamond materials in advanced technologies relevant to the Department of Defense since 1987, has recently undertaken some new projects in diamond research. In collaboration with the Smithsonian Institution Museum of Natural History, NRL researchers have begun studying unique and historic natural colored to understand and characterize the defects/impurities, which cause the color. Many of the properties of diamond necessary for technology are impacted by defects and impurities present in the lattice. NRL has been complementing its studies of these defects and impurities in chemical vapor deposition diamond materials with its studies of natural diamonds at the Smithsonian.

Since late 2005, a team of NRL researchers led by Dr. James Butler of the Chemistry Division, has been examining unusual natural colored diamonds available to the Smithsonian. These included many of the diamonds in the Smithsonian Collection, such at the "Hope" and the "Blue Heart," as well as a collection of 240 fancy colored diamonds in the Aurora Butterfly collection on loan to the Smithsonian.

During 2005, NRL researchers James Butler, Sally Magana (NRC), Jaime Freitas and Paul Klein worked with the Smithsonian, Penn State University, and Ocean Optics to study the optical emission properties of the Hope Diamond. This work, "Using Phosphorescence as a Fingerprint for the Hope and Other Blue Diamonds", was published in Geology, 36, 83-86 (2008). Most recently, in 2010, NRL has been working with the Smithsonian and the Gemological Institute of America (GIA) to study another famous blue diamond, the Wittelsbach-Graff diamond. Both the Hope and the Wittelsbach-Graff diamonds are believed to have originated from the same region in India in the 17th century, have similar blue color and nearly identical red/orange phosphorescence when excited by ultra-violet light. Hence, it has been speculated that they might have originated from the same stone. The Wittelsbach-Graff diamond was last seen in public in 1958; then in 2008 Laurence Graff, a diamond dealer, bought it at auction for 16.4 million GBP. Graff had the stone cut and repolished, reducing it from a 35.5 carat stone to a 31 carat stone, compared to the Hope diamond which is 45.52 carats.

The research team studying the Wittelsbach-Graff diamond used a variety of spectroscopic and microscopic analyzes to determine the extreme similarity of the gems, but also observed distinct differences in the dislocation and strain microstructure which suggests that the gems probably did not originate from the same rough stone.

The Wittelsbach-Graff is on display at the Museum of Natural History from February to August 2010 along with the Hope Diamond. This work continues the ongoing collaboration between NRL scientists and the Museum of Natural History on the Hope diamond and other blue diamonds at the Smithsonian which has examined the phosphorescence (due to donor-acceptor recombination), the boron concentration using secondary ion mass spectroscopy, and soon to be published work on the spectroscopic and structural properties of a collection of pink diamonds.

Another aspect of NRL's diamond research collaboration with the Smithsonian involves an interdisciplinary effort to study rare pink diamonds. Many natural pink diamonds derive their color from colored bands or lamellae in an otherwise colorless diamond. Led by Jeff Post, Eloďse Gaillou, and Tim Rose of the Smithsonian Museum of Natural History; NRL researchers James Butler (Chemistry Division), Rhonda Stroud and Nabil Bassim (Materials Science and Technology Division); along with Alexander Zaitsev, CUNY; and Marc Fries, JPL/Cal Tech studied a suite of natural pink diamonds. The research team used a variety of spectroscopic and microanalytical tools to study the structure, defects, and impurities in and around the colored lamellae.

Pink diamonds are extremely rare, on a par with blue diamonds in rarity and value. But unlike most blue diamonds where the color is caused by an impurity atom, boron, pink diamonds seem to derive their color from structural, or a combination of structural and impurity related defects.

While the research team has not identified the exact structure of the defects causing the pink color, they have determined that it is contained in narrow colored lamellae in an otherwise clear matrix of diamond. Using a focused ion beam microscope, NRL researchers extracted cross-sections of the pink lamella for detailed examination in a transmission electron microscope (TEM). TEM examination of the lattice structure, combined with spectroscopic analysis, suggest that the lamellae are the result of plastic deformation, which occurred while the diamond was still in the earth's mantle and before it was transported to the surface in ancient volcanic eruptions. They will continue their studies to characterize a suite of rare pink diamonds to see if they can fully identify the nature and cause of the defects which cause the pink color. "The pink lamella are twin domains, with atoms arranged to mirror almost exactly those of the surrounding clear diamond. The real question is, what subtle shift in the atomic arrangement makes the twins pink but leaves the nearly identical sibling colorless? The sub-angstrom imaging capabilities of the latest generation of electron microscopes should tell us the answer," says Stroud.

"Understanding these unique colored natural diamonds provides knowledge useful to both technologists and gemologists," Butler explains. "A better understanding of these defects and impurities (dopants) allow us to tailor the materials properties of diamond materials: from electrically insulating to semiconducting; from optically transparent to a variety of colors; or to provide the isolated quantum states for quantum cryptography or quantum computing."

Explore further: Researchers to Study Properties of the Hope Diamond

Related Stories

Researchers to Study Properties of the Hope Diamond

August 25, 2005

Since January, scientists from the Naval Research Laboratory's Chemistry Division have been studying the optical properties of the Hope Diamond, at the invitation of the Smithsonian Institution. In collaboration with the ...

Hope Diamond's phosphorescence key to fingerprinting

January 7, 2008

Shine a white light on the Hope Diamond and it will dazzle you with the brilliance of an amazing blue diamond. Shine an ultraviolet light on the Hope Diamond and the gem will glow red-orange for about five minutes. This phosphorescent ...

Meteorite yields carbon crystals harder than diamond

February 3, 2010

( -- Two new types of ultra-hard carbon crystals have been found by researchers investigating the ureilite class Haverö meteorite that crashed to Earth in Finland in 1971. Ureilite meteorites are carbon-rich ...

Diamond is one tough cookie

January 26, 2010

( -- Most people know that diamond is one of the hardest solids on Earth, so strong that it can easily cut through glass and steel. Surprisingly, very little is known about the strength of diamond at extreme conditions. ...

Recommended for you

Scientific advances can make it easier to recycle plastics

November 17, 2017

Most of the 150 million tons of plastics produced around the world every year end up in landfills, the oceans and elsewhere. Less than 9 percent of plastics are recycled in the United States, rising to about 30 percent in ...

The spliceosome—now available in high definition

November 17, 2017

UCLA researchers have solved the high-resolution structure of a massive cellular machine, the spliceosome, filling the last major gap in our understanding of the RNA splicing process that was previously unclear.

Ionic 'solar cell' could provide on-demand water desalination

November 15, 2017

Modern solar cells, which use energy from light to generate electrons and holes that are then transported out of semiconducting materials and into external circuits for human use, have existed in one form or another for over ...

1 comment

Adjust slider to filter visible comments by rank

Display comments: newest first

not rated yet Mar 28, 2010
Literature says, pink diamonds are positively doped with nitrogen or fluorine. They correspond red sand paper, whereas the N-doped blue diamonds correspond the green one.

Please sign in to add a comment. Registration is free, and takes less than a minute. Read more

Click here to reset your password.
Sign in to get notified via email when new comments are made.