Size-specific cracking shakes out at the nanoscale

Aug 01, 2008
Scanning electron microscope images of a cerium hydride stacked-plate nanostructure. a Typical stacked-plate cluster. b Close-up view of the edges of the plates in a. c Close-up view of another particle showing a finer fracture scale.

(PhysOrg.com) -- Certain sizes of nanostructures may be more susceptible to failure by fracture than others. That is the result of new research by LLNL's Michael Manley and colleagues from Los Alamos National Laboratory that appears as a Rapid Communication in the journal Physical Review B.

As the size of a structure gets to the nanoscale, atomic vibrations (also known as phonons) begin to feel its size and shape in an effect called phonon confinement.

While these effects play an important role in thermal transport, electronic processes and thermodynamic stability, not much is known about their role in fracture.

However, in the new research, the scientists found that at a certain thickness, excess entropy of the confined vibrations reduces the fracture energy and results in a size-specific fracture.

Manley and the Los Alamos team found that particles formed during the reaction of cerium with hydrogen (cerium hydride) fractured into stacked plates. The plates exhibited two thickness scales, one at 100 nanometers, and an additional scale at 30-nanometer scale.

"When the fracture results in nanoplates, it leads to a low level of fracture energy at a certain size, resulting in a size-specific fracture," Manley said. "This has important implications for the design of nanostructures."

"It also may prove useful in the deliberate creation of large quantities of stable nanostructures," he said.

Manley said the time scale for phonon excitations typically occurs in picoseconds, while crack growth is a slower process involving the simultaneous displacement of many planes of atoms over a relatively large distance compared to atomic vibrations. "Thus, the phonon confinement should occur instantaneously as the crack propagates," he said.

Unlike with thermodynamic stability, fracture is a weak-link process, meaning that even a local weakening could be important in dictating the fracture process.

"This could have important consequences, not only for small materials, but also for the way cracks propagate in nanostructured bulk materials," Manley said.

Provided by Lawrence Livermore National Laboratory

Explore further: Chemist develops X-ray vision for quality assurance

add to favorites email to friend print save as pdf

Related Stories

Recommended for you

Chemist develops X-ray vision for quality assurance

12 minutes ago

It is seldom sufficient to read the declaration of contents if you need to know precisely what substances a product contains. In fact, to do this you need to be a highly skilled chemist or to have genuine ...

The future of ultrashort laser pulses

20 minutes ago

Rapid advances in techniques for the creation of ultra-short laser pulses promise to boost our knowledge of electron motions to an unprecedented level.

IHEP in China has ambitions for Higgs factory

17 hours ago

Who will lay claim to having the world's largest particle smasher?. Could China become the collider capital of the world? Questions tease answers, following a news story in Nature on Tuesday. Proposals for ...

The physics of lead guitar playing

19 hours ago

String bends, tapping, vibrato and whammy bars are all techniques that add to the distinctiveness of a lead guitarist's sound, whether it's Clapton, Hendrix, or BB King.

The birth of topological spintronics

20 hours ago

The discovery of a new material combination that could lead to a more efficient approach to computer memory and logic will be described in the journal Nature on July 24, 2014. The research, led by Penn S ...

User comments : 0