Fujitsu Develops Technology for Low-Temperature Full-Service Direct Formation of Graphene Transistors on Large-Scale Sub

November 27, 2009
Figure 1: Graphene

Fujitsu Laboratories today announced, as a world first, the development of a novel technology for forming graphene transistors directly on the entire surface of large-scale insulating substrates at low temperatures while employing chemical-vapor deposition (CVD) techniques which are in widespread use in semiconductor manufacturing.

Compared to the temperatures of 800-1000°C at which graphene is formed with conventional methods, Fujitsu has succeeded in significantly lowering the graphene fabrication-temperature to 650°C, thus allowing for graphene to be formed directly on a variety of insulator substrates, including substrates that are sensitive to the higher temperatures. Graphene is a nano-scale (nano-carbon) with the potential to be the material used in next-generation low-voltage, low-power transistors, as graphene features high-electron and hole mobility characteristics.

Details of this technology will be presented at the Materials Research Society 2009 (MRS 2009) Fall Meeting, to be held from November 30 to December 4 in Boston.

Currently, silicon is the material used for transistor channels - the conduits that pass electricity - in LSIs, and through miniaturization of devices, higher speeds and lower have been realized. However, in recent years, miniaturization technology has been approaching its limits, and achieving further higher performance is becoming increasingly more difficult. This issue has led to a wave of active development of next-generation transistors using materials such as , , or graphene as channel materials.

Graphene is essentially a single layer of the multi-layered graphite that is used, for example, as pencil lead. The individual in graphene are linked into a hexagonal lattice that is laid out in a flat sheet (Figure 1). Single sheets of graphene were first separated successfully in 2004, and were found to feature excellent . Experiments showed that graphene has extremely high electron mobility compared to silicon that is typically used in semiconductors, and it is anticipated that graphene could be used to produce fast, low-voltage transistors.

Figure 2: Graphene transistors formed on a 75mm-diameter silicon (Si) substrate (wafer) with oxide film

Prototype transistors using graphene have been produced since several years ago. Laying the graphene on the substrate involved one of the following procedures:

1. Peel-off/transfer method
A method in which a layer is peeled off from a graphite crystal using tape, and transferred to the substrate.

2. CVD/transfer method
A method in which graphene is formed on a film of metallic catalyst at temperatures of approximately 800-1000°C, and then transferred to a different substrate.

3. Silicon-carbide (SiC) surface decomposition method
A method in which a substrate of SiC, a semiconductor, is heat-treated at 1200-1500°C to form graphene on the SiC surface.

The CVD/transfer method using a metallic catalyst has the advantage that graphene can be formed on any kind of substrate, but because it is impossible to form transistors on conductive metal, the graphene that had been formed on one substrate would be transferred to an insulating substrate to make the transistors. The CVD/transferring method is prone to forming wrinkles in the thin-film graphene, and is not readily amenable to use with the 300-mm wafer size that is common today. Practical implementation of the CVD/transferring method would require the ability to produce transistors that are consistent regardless of substrate size.

An additional issue is that as graphene transistors are usually formed at temperatures of 800°C or higher, there was a limit to the types of substrates that graphene could be used with.

Figure 3: Graphene synthesized in various thicknesses

Overview of Fujitsu's Newly-Developed Technology

As a world first, Fujitsu Laboratories developed novel technology that allows for graphene to be formed on insulating film substrate via CVD at the low fabrication-temperature of 650°C, enabling graphene-based transistors to be directly formed on the entire surface of substrates. Although the test substrate employed was a 75-mm silicon substrate (wafer) with oxide film, the new technique is applicable to larger 300-mm wafers as well (Figure 2). Key details of the new technology are as follows:

1. Low-temperature synthesis of multi-layer graphene featuring thickness controlled via CVD, on entire surface of substrate

Fujitsu Laboratories developed technology in which an iron film catalyst is deposited on a silicon substrate with oxide film, and on top of that, a layer of graphene is formed to a controlled thickness via CVD with acetylene as the feedstock. As illustrated in Figure 3, this technique can be used to form graphene in varied thicknesses anywhere from 1 nm - for few-layer graphene - to 50 nm, for multi-layer graphene. Furthermore, Fujitsu Laboratories' proprietary CVD technology enables a synthesis temperature of 650°C to be achieved, as compared with the typical 800-1000°C, thereby indicating that graphene could be formed on various substrate surfaces other than silicon - such as glass, which is vulnerable to heat.

2. Process for forming transfer-free graphene transistors

Fujitsu Laboratories also developed a process for forming transistors that use graphene as the channel material (Figure 4), as outlined below. This process is independent of wafer size, so it can be applied to large-scale substrates.

1. First, an iron catalyst is formed into the desired channel shape, using a conventional photolithographic process.

2. Graphene is then formed on the iron layer via CVD.

3. Source and drain electrodes of titanium-gold film are formed at both ends of the graphene, thereby "fixing" the graphene.

4. Next, just the iron catalyst is removed using acid, leaving the graphene suspended between the source and drain electrodes, with the graphene "bridged" between the electrodes.

5. Using atomic-layer deposition (ALD), a method for forming thin films, a layer of hafnium dioxide (HfO2) is grown on top of the graphene to stabilize the graphene.

6. Finally, a gate electrode is formed on top of the graphene and through the HfO2, resulting in the formation of a graphene transistor.

Figure 4: Graphene transistor formation process

In order for the performance of graphene transistors to be improved, it is essential that graphene can be formed so that it is suspended in air - as aforementioned in "4" above - so that both sides of the graphene can be cleaned. The ALD method employed by Fujitsu Laboratories allows for the formation of film so that it covers the graphene suspended in air (Figure 5).

This new technology from Fujitsu Laboratories enables successful formation of graphene transistors across the entire surface of a large substrate. Figure 6 illustrates an example of the relationship (dependency) between drain current and gate voltage for a top-gate graphene transistor. The figure clearly shows the ambipolar characteristics that are particular to graphene.

As graphene at the thickness of a few nanometers is transparent and passes light well, it is a candidate for use as the channel and electrode material in thin-film transistors used in video displays. With Fujitsu Laboratories' new technology the graphene-forming temperature is approximately 650°C, and is not far from the temperature of approximately 550°C at which graphene could be formed directly on conventional glass. Thus, it is feasible that in the near future it may be possible to form graphene transistors directly on large glass substrates.

Figure 6: Optical microscope image of a top-gate transistor and its cross-sectional Transmission Electron Microscope (TEM) image

Figure 5: Schematic diagram of a suspended graphene transistor and its cross-sectional Transmission Electron Microscope (TEM) image
Provided by Fujitsu Laboratories

Explore further: Scientists Develop World's Fastest Graphene Transistor

Related Stories

Scientists Develop World's Fastest Graphene Transistor

December 19, 2008

( -- IBM Researchers today announced that they demonstrated the operation of graphene field-effect transistors at GHz frequencies, and achieved the highest frequencies reported so far using this novel non-silicon ...

AMO Manufactures First Graphene Transistors

February 8, 2007

In the scope of his innovative project ALEGRA the AMO nanoelectronics group of Dr. Max Lemme was able to manufacture top-gated transistor-like field-effect devices from monolayer graphene.

Light-speed nanotech: Controlling the nature of graphene

January 21, 2009

Researchers at Rensselaer Polytechnic Institute have discovered a new method for controlling the nature of graphene, bringing academia and industry potentially one step closer to realizing the mass production of graphene-based ...

A Smarter Way to Grow Graphene

May 14, 2008

Graphene, a sheet of carbon just one atom thick, has many potential uses in the electronics industry, but producing these ideal two-dimensional carbon sheets is very difficult and, as a result, their use has been stifled ...

Unzipping Carbon Nanotubes Can Make Graphene Ribbons

April 20, 2009

( -- By "unzipping" carbon nanotubes, researchers have shown how to make flat graphene ribbons. Graphene, which is a one-atom-thick sheet of carbon that looks like chicken wire, has unique electrical properties ...

Recommended for you

Samsung to disable Note 7 phones in recall effort

December 9, 2016

Samsung announced Friday it would disable its Galaxy Note 7 smartphones in the US market to force remaining owners to stop using the devices, which were recalled for safety reasons.

Swiss unveil stratospheric solar plane

December 7, 2016

Just months after two Swiss pilots completed a historic round-the-world trip in a Sun-powered plane, another Swiss adventurer on Wednesday unveiled a solar plane aimed at reaching the stratosphere.

Solar panels repay their energy 'debt': study

December 6, 2016

The climate-friendly electricity generated by solar panels in the past 40 years has all but cancelled out the polluting energy used to produce them, a study said Tuesday.


Adjust slider to filter visible comments by rank

Display comments: newest first

Nov 27, 2009
This comment has been removed by a moderator.
not rated yet Nov 28, 2009
One of the most important articles of the year! This is a major breakthrough in making smaller, faster and low energy consumption chips!
not rated yet Nov 28, 2009
from lab to fab, major milestone!
Especially since the process fits within the current production lines and wafer sizes of the silicon industry, this has the potential to bring graphene from the realm of the exotic to your pc before 2015 instead of 2020
not rated yet Nov 28, 2009
Its a bit of a rubbish transistor though isn't it - the on/off ratio is about 1.01. you can't switch it off even with a negative gate voltage, this switches it back on.

oh well, the first germanium transistors were very poor, but at least they were linear.
not rated yet Nov 30, 2009

Where did you get the on/off ratio? I couldn't find it anywhere.

Please sign in to add a comment. Registration is free, and takes less than a minute. Read more

Click here to reset your password.
Sign in to get notified via email when new comments are made.